Towards metal free supported quaternary ammonium halides catalysts for an optimized cycloaddition of CO 2 onto styrene oxide
Résumé
The present work reports on a large selection of porous siliceous materials functionalised by quaternary ammonium salts (QAS) with various pores structures, possible doping with Zn2+, and different ammonium salt substituents as well as halide counter-ions. After characterization by TGA, N2 physisorption, XRD, XPS and 13C NMR, the latter were tested as catalysts for the cycloaddition of CO2 onto styrene oxide to produce styrene carbonate. Control experiments performed with the naked silica supports and soluble QAS demonstrated the synergistic action of the silanol groups on the supports and the quaternary ammonium salts. Most importantly it was also shown that covalent grafting confirmed the trend, without reducing the catalytic activity in comparison with conditions where soluble QAS were used. However, the possibility to recycle the entire catalytic system is an obvious benefit of heterogenized QAS. Quite clearly, our work highlighted the higher catalytic efficiency of the most hindered quaternary ammonium salt (butyl groups) combined with bromide ions. The resulting catalysts were tested under three types of conditions: in dichloromethane at 3 mol% at 100°C under 10 bar of CO2, in benzonitrile at 0.8 mol% at 80°C under 10 bar of CO2 and in the absence of solvent at 0.2 mol% at 100°C under 20 bar of CO2. Much better TOF values, of the order of 40 to 50 h-1, were obtained in the latter two cases. Finally, the advantages and disadvantages of these last two catalytic systems are discussed, particularly with regard to the development of a more sustainable chemistry.
Domaines
ChimieOrigine | Fichiers produits par l'(les) auteur(s) |
---|